Material: | Q195,Q235 and so on |
Surface treatment: | Hot-dipped galvanized,electro galvanized,black,PVC coated |
Wire diameter: | 0.2mm-4mm |
Roll weight: | 1kg-25kg,or as your request |
Zinc coated: | 10g/SQM-200g/SQM or as your request |
Color: | green,white,yellow |
Company Info. |
Anping Yaqi Wire Mesh Co.,Ltd |
View Contact Details |
Product List |
Low Carbon Steel And High Carbon Steel , Hot - Dipped Galvanized
Binding Wire 0.2mm-4mm
Product Introduction
Wire is available in both low carbon and high carbon quality steel.
Low carbon wire is available as galvanized, bright, and annealed
with wire processing options that include cold heading and
straighten and cut. Used primarily for components in applications
such as the construction, automotive and military. Carbon steel
wire comes in diameters that range from 0.008” to 1.25” depending
on the type. This type of carbon wire forms easily and can handle
moderate flattening and bending.
Main production processes for galvanized wire are as follows:
Step 1. Galvanized wire's first stage is drawing:
there are two kinds of drawing machine: powder drawing and water drawing.
Powder drawing is fit for junior drawing(6.5mm~4.0mm). One powder drawing machine has 4 tanks and 4 molds. One tank is matched with a mold. Each of them are offered energy by a electromotor. 0.9mm(max)can be "eat" when the wire cross a mold. There are no loss of weight during drawing. Powder is used as lubricant, which is made of soap and butter. Mold is hidden behind the powder.
Water draw is used for senior draw.(≤4.0mm)The container is filled with water, soap and 8 molds. Compared with powder draw, water draw can save lots of room and the wire cannot be broken.
Step 2. Galvanized wire's second stage is anneal:
After drawing, the wire is thinner, but also very hard. The tensile strength is about 700N. These wire can be used to produce nail and mesh panel. For galvanized wire, it still need annealing
Anneal is to low the tensile strength of wire. The stove is solid and built with red bricks. The architecture of anneal stove is cuboid. Different thickness of wire require different temperature. Range is from 700°C to 900°C. Output of the anneal stove, the tensile strength is 400N~600N.
Step 3. Galvanized wire's third stage is chlorhydric acid washing:
After the draw and anneal, the wire is thinner, softer but also much more dirty. It needs chlorhydric acid washing to remove the impurities. Chlorhydric acid washing requires water pool and chlorhydric acid pool. The density
of chlorhydric acid is 17%. In the Chlorhydric acid pool, there is a caldron used for the emission of vapor.
Step 4 . Galvanized wire's fourth stage: Zinc coating:
After the chlorhydric acid pool, water pool is also necessary. In the zinc pool, displacement reaction is chemical and uniformly distributed. The surface of wire is smooth. Because wire cross the zinc pool fast, abundant zinc coating requires 4 zinc pools.
Product Feature
Product Application
Galvanized steel wire/iron wire is widely used in industry,
agriculture, farming, construction, transport, mining and other
fields,Such as steel wire mash ,machine protective cover, animal
livestock fence, flowers and trees fences, window guards, poultry
cage bar, channel, crawl and home office food basket, paper basket
and decoration articles,Planting greenhouses, farms, cotton
packing, springs and wire rope manufacturing etc
Product Specification
.HS | product | dia (mm) |
|
| elongation |
|
72172000 | galvanized wire | 0.20-0.55 | ±0.01 | 300--400 | min 15% | min 20 |
0.20-0.55 | ±0.01 | 300--400 | min 20 | |||
0.56-1.60 | ±0.02 | 300--500 | min 25 | |||
1.80-6.00 | ±0.02 | 400--1400 | min12% | 50-350 | ||
±0.03 | max 5% | |||||
electro |
| ±0.01 | 300--370 | min15% | 10--15 | |
| ±0.01 | 300--490 | min15% | |||
| ±0.02 | max550 | min15% | 10--50 |